The ab-plane resistivity of Ba(Fe1-xRux)2As2 (x = 0.00, 0.09, 0.16, 0.21, and 0.28) was studied under nearly hydrostatic pressures, up to 7.4 GPa, in order to explore the T-P phase diagram and to compare the combined effects of iso-electronic Ru substitution and pressure. The parent compound BaFe2As2 exhibits a structural/magnetic phase transition near 134 K. At ambient pressure, progressively increasing Ru concentration suppresses this phase transition to lower temperatures at the approximate rate of ~5 K/% Ru and is correlated with the emergence of superconductivity. By applying pressure to this system, a similar behavior is seen for each concentration: the structural/magnetic phase transition is further suppressed and superconductivity induced and ultimately, for larger x Ru and P, suppressed. A detailed comparison of the T-P phase diagrams for all Ru concentrations shows that 3 GPa of pressure is roughly equivalent to 10% Ru substitution. Furthermore, due to the sensitivity of Ba(Fe1-xRux)2As2 to pressure conditions, the melting of the liquid media, 4 : 6 light mineral oil : n-pentane and 1 : 1 iso-pentane : n-pentane, used in this study could be readily seen in the resistivity measurements. This feature was used to determine the freezing curves for these media and infer their room temperature, hydrostatic limits: 3.5 and 6.5 GPa, respectively.
تحميل البحث