تسجيل مستخدم جديدTuning the electrical conductivity of Pt-containing granular metals by postgrowth electron irradiation
140
0
0.0
(
0
)
اسأل ChatGPT حول البحث
ﻻ يوجد ملخص باللغة العربية
We have fabricated Pt-containing granular metals by focused electron beam induced deposition from the $(CH_3)_3CH_3C_5H_4Pt$ precursor gas. The granular metals are made of platinum nanocrystallites embedded in a carbonaceous matrix. We have exposed the as-grown nanocomposites to low energy electron beam irradiation and we have measured the electrical conductivity as a function of the irradiation dose. Postgrowth electron beam irradiation transforms the matrix microstructure and thus the strength of the tunneling coupling between Pt nanocrystallites. For as-grown samples (weak tunnel coupling regime) we find that the temperature dependence of the electrical conductivity follows the stretched exponential behavior characteristic of the correlated variable-range hopping transport regime. For briefly irradiated samples (strong tunnel coupling regime) the electrical conductivity is tuned across the metal-insulator transition. For long-time irradiated samples the electrical conductivity behaves like that of a metal. In order to further analyze changes of the microstructure as a function of the electron irradiation dose we have carried out transmission electron microscope (TEM), micro-Raman and atomic force microscopy (AFM) investigations. TEM pictures reveal that the crystallites size of long-time irradiated samples is larger than that of as-grown samples. Furthermore we do not have evidence of microstructural changes in briefly irradiated samples. By means of micro-Raman we find that by increasing the irradiation dose the matrix changes following a graphitization trajectory between amorphous carbon and nanocrystalline graphite. Finally, by means of AFM measurements we observe a reduction of the volume of the samples with increasing irradiation time which we attribute to the removal of carbon molecules.
قيم البحث
اقرأ أيضاً
The delafossite metals PdCoO$_{2}$, PtCoO$_{2}$ and PdCrO$_{2}$ are among the highest conductivity materials known, with low temperature mean free paths of tens of microns in the best as-grown single crystals. A key question is whether these very low
resistive scattering rates result from strongly suppressed backscattering due to special features of the electronic structure, or are a consequence of highly unusual levels of crystalline perfection. We report the results of experiments in which high energy electron irradiation was used to introduce point disorder to the Pd and Pt layers in which the conduction occurs. We obtain the cross-section for formation of Frenkel pairs in absolute units, and cross-check our analysis with first principles calculations of the relevant atomic displacement energies. We observe an increase of resistivity that is linear in defect density with a slope consistent with scattering in the unitary limit. Our results enable us to deduce that the as-grown crystals contain extremely low levels of in-plane defects of approximately $0.001%$. This confirms that crystalline perfection is the most important factor in realizing the long mean free paths, and highlights how unusual these delafossite metals are in comparison with the vast majority of other multi-component oxides and alloys. We discuss the implications of our findings for future materials research.
Polar metals are an intriguing class of materials that simultaneously host free carriers and polar structural distortions. Despite the name polar metal, however, most well-studied polar metals are poor electrical conductors. Here, we demonstrate the
molecular beam epitaxial (MBE) growth of LaPtSb and LaAuGe, two polar metal compounds whose electrical resistivity is an order of magnitude lower than the well studied oxide polar metals. These materials belong to a broad family of $ABC$ intermetallics adopting the stuffed wurtzite structure, also known as hexagonal Heusler compounds. Scanning transmission electron microscopy (STEM) reveals a polar structure with unidirectionally buckled $BC$ (PtSb, AuGe) planes. Magnetotransport measurements demonstrate good metallic behavior with low residual resistivity ($rho_{LaAuGe}=59.05$ $muOmegacdot$cm and $rho_{LaAPtSb}=27.81$ $muOmegacdot$cm at 2K) and high carrier density ($n_hsim 10^{21}$ cm$^{-3}$). Photoemission spectroscopy measurements confirm the band metallicity and are in quantitative agreement with density functional theory (DFT) calculations. Through DFT-Chemical Pressure and Crystal Orbital Hamilton Population analyses, the atomic packing factor is found to support the polar buckling of the structure, though the degree of direct interlayer $B-C$ bonding is limited by repulsion at the $A-C$ contacts. When combined with insulating hexagonal Heuslers, these materials provide a new platform for fully epitaxial, multiferroic heterostructures.
W-based granular metals have been prepared by electron beam induced deposition from the tungsten-hexacarbonyl W(CO)6 precursor. In situ electrical conductivity measurements have been performed to monitor the growth process and to investigate the beha
vior of the deposit under electron beam post irradiation and by exposure to air. During the first part of the growth process, the electrical conductivity grows non-linearly, independent of the electron beam parameters. This behavior is interpreted as the result of the increase of the W-particles diameter. Once the growth process is terminated, the electrical conductivity decreases with the logarithm of time, sigma ln(t). Temperature-dependent conductivity measurements of the deposits reveal that the electrical transport takes place by means of electron tunneling either between W-metal grains or between grains and trap sites in the matrix. After venting the electron microscope the electrical conductivity of the deposits shows a degradation behavior, which depends on the composition. Electron post-irradiation increases the electrical conductivity of the deposits.
Carbon nanotubes are a good realization of one-dimensional crystals where basic science and potential nanodevice applications merge. Defects are known to modify the electrical resistance of carbon nanotubes. They can be present in as-grown carbon nan
otubes, but controlling externally their density opens a path towards the tuning of the nanotube electronic characteristics. In this work consecutive Ar+ irradiation doses are applied to single-walled nanotubes (SWNTs) producing a uniform density of defects. After each dose, the room temperature resistance versus SWNT-length [R(L)] along the nanotube is measured. Our data show an exponential dependence of R(L) indicating that the system is within the strong Anderson localization regime. Theoretical simulations demonstrate that mainly di-vacancies contribute to the resistance increase induced by irradiation and that just a 0.03% of di-vacancies produces an increase of three orders of magnitude in the resistance of a 400 nm SWNT length.
The ability to engineer the thermal conductivity of materials allows us to control the flow of heat and derive novel functionalities such as thermal rectification, thermal switching, and thermal cloaking. While this could be achieved by making use of
composites and metamaterials at bulk scales, engineering the thermal conductivity at micro- and nano-scale dimensions is considerably more challenging. In this work we show that the local thermal conductivity along a single Si nanowire can be tuned to a desired value (between crystalline and amorphous limits) with high spatial resolution through selective helium ion irradiation with a well-controlled dose. The underlying mechanism is understood through molecular dynamics simulations and quantitative phonon-defect scattering rate analysis, where the behavior of thermal conductivity with dose is attributed to the accumulation and agglomeration of scattering centers at lower doses. Beyond a threshold dose, a crystalline-amorphous transition was observed.
سجل دخول لتتمكن من نشر تعليقات
التعليقات
جاري جلب التعليقات
سجل دخول لتتمكن من متابعة معايير البحث التي قمت باختيارها