In this cross-sectional scanning tunneling microscopy study we investigated various techniques to control the shape of self-assembled quantum dots (QDs) and wetting layers (WLs). The result shows that application of an indium flush during the growth of strained InGaAs/GaAs QD layers results in flattened QDs and a reduced WL. The height of the QDs and WLs could be controlled by varying the thickness of the first capping layer. Concerning the technique of antimony capping we show that the surfactant properties of Sb result in the preservation of the shape of strained InAs/InP QDs during overgrowth. This could be achieved by both a growth interrupt under Sb flux and capping with a thin GaAsSb layer prior to overgrowth of the uncapped QDs. The technique of droplet epitaxy was investigated by a structural analysis of strain free GaAs/AlGaAs QDs. We show that the QDs have a Gaussian shape, that the WL is less than 1 bilayer thick, and that minor intermixing of Al with the QDs takes place.
Hydrogenation of nitrogen (N) doped GaAs allows for reversible tuning of the bandgap and the creation of site controlled quantum dots through the manipulation of N-nH complexes, N-nH complexes, wherein a nitrogen atom is surrounded by n hydrogen (H)
Silicon (Si) donors in GaAs have been the topic of extensive studies since Si is the most common and well understood n-type dopant in III-V semiconductor devices and substrates. The indirect bandgap of AlAs compared to the direct one of GaAs leads to
We present results on the direct spatial mapping of the wave-function of a hole bound to a Mn acceptor in GaAs. To investigate individual Mn dopants at the atomic scale in both ionized and neutral configurations, we used a room temperature cross-sect
Cross-sectional scanning tunneling microscopy (X-STM) was employed to characterize the InAs submonolayer quantum dots (SMLQDs) grown on top of a Si-doped GaAs(001) substrate in the presence of (2X4) and c(4X4) surface reconstructions. Multiple layers
An individual Mn acceptor in GaAs is mapped by Cross-sectional Scanning Tunneling Microscopy (X-STM) at room temperature and a strongly anisotropic shape of the acceptor state is observed. An acceptor state manifests itself as a cross-like feature wh