Magnetic nanoparticles (NP) of magnetite (Fe3O4) coated with oleic acid (OA) and dodecanoic acid (DA) were synthesized and investigated through Transmission Electron Microscopy (TEM),magnetization M, and ac magnetic susceptibility measurements. The OA coated samples were produced with different magnetic concentrations (78, 76, and 65%) and the DA sample with 63% of Fe3O4. Images from TEM indicate that the NP have a nearly spherical geometry and mean diameter ~ 5.5 nm. Magnetization measurements, performed in zero field cooled (ZFC) and field cooled (FC) processes under different external magnetic fields H, exhibited a maximum at a given temperature TB in the ZFC curves, which depends on the NP coating (OA or DA), magnetite concentration, and H. The temperature TB decreases monotonically with increasing H and, for a given H, the increase in the magnetite concentration results in an increase of TB. The observed behavior is related to the dipolar interaction (DI) between NP which seems to be an important mechanism in all samples studied. This is supported by the results of the ac magnetic susceptibility Xac measurements, where the temperature in which X peaks for different frequencies follows the Vogel-Fulcher model, a feature commonly found in systems with dipolar interactions. Curves of H vs. TB/TB(H=0) for samples with different coatings and magnetite concentrations collapse into a universal curve, indicating that the qualitative magnetic behavior of the samples may be described by the NP themselves, instead of the coating or the strength of the dipolar interaction. Below TB, M vs. H curves show a coercive field (HC) that increases monotonically with decreasing temperature. The saturation magnetization (MS) follows the Blochs law and values of MS at room temperature as high as 78 emu/g were estimated, a result corresponding to ~80% of the bulk value. The overlap of M/MS vs. H/T curves for a given sample and the low HC at high temperatures suggest superparamagnetic behavior in all samples studied. The overlap of M/MS vs. H curves at constant temperature for different samples indicates that the NP magnetization behavior is preserved, independently of the coating and magnetite concentration.
قيم البحث
اقرأ أيضاً
Magnetic measurements have been performed on 40-nm sphere-like Fe3O4 nanoparticles using a Quantum Design vibrating sample magnetometer. Coating Fe3O4 nanoparticles with SiO2 effectively eliminates magnetic interparticle interactions so that the coer
cive field HC in the hightemperature range between 300 K and the Curie temperature (855 K) can be well fitted by an expression for noninteracting randomly oriented single-domain particles. From the fitting parameters, the effective anisotropy constant K is found to be (1.68 pm 0.17) times 105 erg/cm3, which is slightly larger than the bulk magnetocrystalline anisotropy constant of 1.35 times 105 erg/cm3. Moreover, the inferred mean particle diameter from the fitting parameters is in quantitative agreement with that determined from transmission electron microscope. Such a quantitative agreement between data and theory suggests that the assemble of our SiO2-coated sphere-like Fe3O4 nanopartles represents a good system of noninteracting randomly-oriented single-domain particles.
Homogeneous single phase GdCrO3 nanoparticles are synthesized by a modified-hydrothermal synthesis. The sample shows a compensation temperature at 128 K, below which the DC magnetization becomes negative and positive at low temperatures due to the co
mpetition between the two sublattice magnetization. At Neel temperature (168K), the line width and the intensity show an abrupt transition, revealed from electron paramagnetic resonance spectroscopy.
Using microemulsion methods, CoO-Pt core-shell nanoparticles (NPs), with diameters of nominally 4 nm, were synthesized and characterized by high-resolution transmission electron microscopy (HRTEM) and a suite of x-ray spectroscopies, including diffra
ction (XRD), absorption (XAS), absorption near-edge structure (XANES), and extended absorption fine structure (EXAFS), which confirmed the existence of CoO cores and pure Pt surface layers. Using a commercial magnetometer, the ac and dc magnetic properties were investigated over a range of temperature (2 K $leq$ T $leq$ 300 K), magnetic field ($leq$ 50 kOe), and frequency ($leq$ 1 kHz). The data indicate the presence of two different magnetic regimes whose onsets are identified by two maxima in the magnetic signals, with a narrow maximum centered at 6 K and a large one centered at 37 K. The magnetic responses in these two regimes exhibit different frequency dependences, where the maximum at high temperature follows a Vogel-Fulcher law, indicating a superparamagnetic (SPM) blocking of interacting nanoparticle moments and the maximum at low temperature possesses a power law response characteristic of a collective freezing of the nanoparticle moments in a superspin glass (SSG) state. This co-existence of blocking and freezing behaviors is consistent with the nanoparticles possessing an antiferromagnetically ordered core, with an uncompensated magnetic moment, and a magnetically disordered interlayer between CoO core and Pt shell.
We propose a new approach to understand the time-dependent temperature increasing process of gold-silica core-shell nanoparticles injected into chicken tissues under near-infrared laser irradiation. Gold nanoshells strongly absorb near-infrared radia
tions and efficiently transform absorbed energy into heat. Temperature rise given by experiments and numerical calculations based on bioheat transfer are in good agreement. Our work improves the analysis of a recent study [Richardson et al., Nano Lett. 9, 1139 (2009)] by including effects of the medium perfusion on temperature increase. The theoretical analysis can also be used to estimate the distribution of nanoparticles in experimental samples and provide a relative accuracy prediction for the temperature profile of new systems. This methodology would provide a novel and reliable tool for speeding up photothermal investigations and designing state-of-the-art photothermal devices.
We present a systematic study of core-shell Au/Fe_3O_4 nanoparticles produced by thermal decomposition under mild conditions. The morphology and crystal structure of the nanoparticles revealed the presence of Au core of <d> = (6.9pm 1.0) nm surrounde
d by Fe_3O_4 shell with a thickness of ~3.5 nm, epitaxially grown onto the Au core surface. The Au/Fe_3O_4 core-shell structure was demonstrated by high angle annular dark field scanning transmission electron microscopy analysis. The magnetite shell grown on top of the Au nanoparticle displayed a thermal blocking state at temperatures below T_B = 59 K and a relaxed state well above T_B. Remarkably, an exchange bias effect was observed when cooling down the samples below room temperature under an external magnetic field. Moreover, the exchange bias field (H_{EX}) started to appear at T~40 K and its value increased by decreasing the temperature. This effect has been assigned to the interaction of spins located in the magnetically disordered regions (in the inner and outer surface of the Fe_3O_4 shell) and spins located in the ordered region of the Fe_3O_4 shell.