تسجيل مستخدم جديدOn Using Magnetic and optical methods to determine the size and characteristics of nanoparticles embedded in oxide semiconductors
122
0
0.0
(
0
)
اسأل ChatGPT حول البحث
ﻻ يوجد ملخص باللغة العربية
Films of oxides doped with transition metals are frequently believed to have magnetic inclusions. Magnetic methods to determine the amount of nanophases and their magnetic characteristics are described. The amount of the sample that is paramagnetic may also be measured. Optical methods are described and shown to be very powerful to determine which defects are also magnetic.
قيم البحث
اقرأ أيضاً
In order to better understand the transition from quantum to classical behavior in spin system, electron magnetic resonance (EMR) is studied in suspensions of superparamagnetic magnetite nanoparticles with an average diameter of ~ 9 nm and analyzed i
n comparison with the results obtained in the maghemite particles of smaller size (~ 5 nm). It is shown that both types of particles demonstrate common EMR behavior, including special features such as the temperature-dependent narrow spectral component and multiple-quantum transitions. These features are common for small quantum systems and not expected in classical case. The relative intensity of these signals rapidly decreases with cooling or increase of particle size, marking gradual transition to the classical FMR behavior.
In this work we studied the influence of particle size and agglomeration in the performance of solid oxide fuel cell cathodes made with nanoparticles of La0.8Sr0.2MnO3. We followed two synthesis routes based on the Liquid Mix method. In both procedur
es we introduced additional reagents in order to separated the manganite particles. We evaluated cathodic performance by Electrochemical Impedance Spectroscopy in symmetrical (CATHODE/ELECTROLYTE/CATHODE) cells. Particle size was tuned by the temperature used for cathode sintering. Our results show that deagglomeration of the particles, serves to improve the cathodes performance. However, the dependence of the performance with the size of the particles is not clear, as different trends were obtained for each synthesis route. As a common feature, the cathodes with the lowest area specific resistance are the ones sintered at the largest temperature. This result indicates that an additional factor related with the quality of the cathode/electrolyte sintering, is superimposed with the influence of particle size, however further work is needed to clarify this issue. The enhancement obtained by deagglomeration suggest that the use of this kind of methods deserved to be considered to develop high performance electrodes for solid oxide fuel cells.
We have studied the magnetic and power absorption properties of a series of magnetic nanoparticles (MNPs) of Fe3O4 with average sizes <d> ranging from 3 to 26 nm. Heating experiments as a function of particle size revealed a strong increase in the sp
ecific power absorption (SPA) values for particles with <d> = 25-30 nm. On the other side saturation magnetization MS values of these MNPs remain essentially constant for particles with <d> above 10 nm, suggesting that the absorption mechanism is not determined by MS. The largest SPA value obtained was 130 W/g, corresponding to a bimodal particle distribution with average size values of 17 and 26 nm.
We present a numerical simulation study of the exchange bias (EB) effect in nanoparticles with core/shell structure aimed to unveil the microscopic origin of some of the experimental phenomenology associated to this effect. In particular, we have foc
used our study on the particle size and field cooling dependence of the hysteresis loop shifts. To this end, hysteresis loops after a field cooling process have been computed by means of Monte Carlo simulations based on a model that takes into account the peculiar properties of the core, shell and interfacial regions of the particle and the EB and coercive fields have been extracted from them. The results show that, as a general trend, the EB field $h_{EB}$ decreases with increasing particle size, in agreement with some experimental observations. However, closer inspection reveals notable oscillations of $h_{EB}$ as a function of the particle radius which we show to be closely related to the net magnetization established after field cooling at the interfacial shell spins. For a particle with ferromagnetic interface coupling, we show that the magnitude and sign of $h_{EB}$ can be varied with the magnetic field applied during the cooling process.
We report a study on the pressure response of the anisotropy energy of hollow and solid maghemite nanoparticles. The differences between the maghemite samples are understood in terms of size, magnetic anisotropy and shape of the particles. In particu
lar, the differences between hollow and solid samples are due to the different shape of the nanoparticles and by comparing both pressure responses it is possible to conclude that the shell has a larger pressure response when compared to the core.
سجل دخول لتتمكن من نشر تعليقات
التعليقات
جاري جلب التعليقات
سجل دخول لتتمكن من متابعة معايير البحث التي قمت باختيارها