The magnetic-field-induced variations of the microwave surface resistance, R_s, have been investigated in ceramic Mg_{1-x}(LiAl)_xB_2, with x in the range 0.1 - 0.4. The measurements have been performed on increasing and decreasing the DC magnetic field, H_0, at fixed temperatures. At low temperatures, we have observed a magnetic hysteresis in the R_s(H_0) curves in all the investigated samples. On increasing the temperature, the range of H_0 in which the hysteretic behavior is visible shrinks; however, in the sample with x = 0.1 it is present up to temperatures close to T_c. We show that the field dependence of R_s can be quantitatively justified taking into account the critical-state effects on the fluxon lattice only in the sample with x = 0.4. On the contrary, in the samples with x < 0.4 the hysteresis exhibits an unusual shape, similar to that observed in others two-gap MgB_2 samples, which cannot be justified in the framework of the critical-state models.
قيم البحث
اقرأ أيضاً
We report on the microwave surface resistance of two polycrystalline Mg11B2 samples; one consists of pristine material, the other has been irradiated at very high neutron fluence. It has already been reported that in the strongly irradiated sample th
e two gaps merge into a single value. The mw surface resistance has been measured in the linear regime as a function of the temperature and the DC magnetic field, at increasing and decreasing fields. The results obtained in the strongly irradiated sample are quite well justified in the framework of a generalized Coffey and Clem model, in which we take into account the field distribution inside the sample due to the critical state. The results obtained in the pristine sample show several anomalies, especially at low temperatures, which cannot be justified in the framework of standard models for the fluxon dynamics. Only at temperatures near Tc and for magnetic fields greater than 0.5Hc2(T) the experimental data can quantitatively be accounted for by the Coffey and Clem model, provided that the upper-critical-field anisotropy is taken into due account.
The microwave power, dc magnetic field, frequency and temperature dependence of the surface resistance of MgB2 films and powder samples were studied. Sample quality is relatively easy to identify by a number of characteristics, the most clear being t
he breakdown in the omega squared law for poor quality samples. Analysis of the experimental data suggests the most attractive procedure for high quality film growth for technical applications.
Microwave-field distribution, dissipation, and surface impedance are theoretically investigated for superconductors with laminar grain boundaries (GBs). In the present theory we adopt the two-fluid model for intragrain transport current in the grains
, and the Josephson-junction model for intergrain tunneling current across GBs. Results show that the surface resistance $R_s$ nonmonotonically depends on the critical current density $J_{cj}$ at GB junctions, and $R_s$ for superconductors with GBs can be smaller than the surface resistance $R_{s0}$ for ideal homogeneous superconductors without GBs.
The two tone intermodulation distortion arising in MgB2 thin films synthesized by hybrid physical-chemical vapour deposition is studied in order to probe the influence of the two bands on the nonlinear response of this superconductor. The measurement
s are carried out by using a dielectrically loaded copper cavity operating at 7 GHz. Microwave data on samples having critical temperatures above 41 K, very low resistivity values, and residual resistivity ratio larger than 10, are shown. The dependence of the nonlinear surface losses and of the third order intermodulation products on the power feeding the cavity and on the temperature is analyzed. At low power, the signal arising from distortion versus temperature shows the intrinsic s-wave behavior expected for this compound. Data are compared with measurements performed on Nb and YBCO thin films using the same technique.
We discuss on the electromagnetic response of a polycrystalline sample of LaO_0.94F_0.06FeAs exposed to DC magnetic fields up to 10 kOe. The low- and high-frequency responses have been investigated by measuring the AC susceptibility at 100 kHz and th
e microwave surface resistance at 9.6 GHz. At low as well as high DC magnetic fields, the susceptibility strongly depends on the amplitude of the AC driving field, highlighting enhanced nonlinear effects. The field dependence of the AC susceptibility exhibits a magnetic hysteresis that can be justified considering the intragrain-field-penetration effects on the intergrain critical current density. The microwave surface resistance exhibits a clockwise magnetic hysteresis, which cannot be justified in the framework of the critical-state models of the Abrikosov-fluxon lattice; it may have the same origin as that detected in the susceptibility.
سجل دخول لتتمكن من نشر تعليقات
التعليقات
جاري جلب التعليقات
سجل دخول لتتمكن من متابعة معايير البحث التي قمت باختيارها