تسجيل مستخدم جديد3D nanostructuring of La0.7Sr0.3MnO3 thin film surfaces by scanning tunnelling microscopy
292
0
0.0
(
0
)
اسأل ChatGPT حول البحث
ﻻ يوجد ملخص باللغة العربية
Nanoscale 3D surface modifications, by scanning tunneling microscopy under ambient conditions, of La0.7Sr0.3MnO3 thin films have been performed. It was demonstrated that there are well defined combinations of bias voltages and scan speeds which allow for controlled surface structuring. Lateral structures with sizes down to 1.5 nm are possible to obtain. Moreover, it is possible to reproducibly control the depth of etching with half a unit cell precision, enabling design of 3D surface structures and control of the surface termination of La0.7Sr0.3MnO3 through etching.
قيم البحث
اقرأ أيضاً
Scanning tunnelling spectroscopy measurements were performed on La0.7Sr0.3MnO3 thin films both at room temperature and liquid nitrogen temperature. While no inhomogeneities were recorded at liquid nitrogen temperature on any sample, a clear evidence
of spectroscopic inhomogeneities was evident in tunnelling conductance maps collected at room temperature. The investigated films exhibit a transition from a ferromagnetic-metallic to a paramagnetic-insulating state around room temperature, so that the observed spectroscopic features can be interpreted within a phase separation scenario. A quantitative analysis of the observed spectroscopic features is reported pointing out the occurrence of phase modulation and its possible correlation with the properties of the system.
Positron annihilation lifetime spectroscopy (PALS) and positron-electron momentum density (PEMD) studies on multilayers of PbSe nanocrystals (NCs), supported by transmission electron microscopy (TEM), show that positrons are strongly trapped at NC su
rfaces, where they provide insight into the surface composition and electronic structure of PbSe NCs. Our analysis indicates abundant annihilation of positrons with Se electrons at the NC surfaces and with O electrons of the oleic ligands bound to Pb ad-atoms at the NC surfaces, which demonstrates that positrons can be used as a sensitive probe to investigate the surface physics and chemistry of nanocrystals inside multilayers. Ab-initio electronic structure calculations provide detailed insight in the valence and semi-core electron contributions to the positron-electron momentum density of PbSe. Both lifetime and PEMD are found to correlate with changes in the particle morphology characteristic of partial ligand removal.
An in situ tip preparation procedure compatible with ultra-low temperature and high magnetic field scanning tunneling microscopes is presented. This procedure does not require additional preparation techniques such as thermal annealing or ion milling
. It relies on the local electric-field-induced deposition of material from the tip onto the studied surface. Subsequently, repeated indentations are performed onto the sputtered cluster to mechanically anneal the tip apex and thus to ensure the stability of the tip. The efficiency of this method is confirmed by comparing the topography and spectroscopy data acquired with either unprepared or in situ prepared tips on epitaxial graphene grown on Ru (0001). We demonstrate that the use of in situ prepared tips increases the stability of the scanning tunneling images and the reproducibility of the spectroscopic measurements.
Electrical field control of the carrier density of topological insulators (TI) has greatly expanded the possible practical use of these materials. However, the combination of low temperature local probe studies and a gate tunable TI device remains ch
allenging. We have overcome this limitation by scanning tunneling microscopy and spectroscopy measurements on in-situ molecular beam epitaxy growth of Bi2Se3 films on SrTiO3 substrates with pre-patterned electrodes. Using this gating method, we are able to shift the Fermi level of the top surface states by 250 meV on a 3 nm thick Bi2Se3 device. We report field effect studies of the surface state dispersion, band gap, and electronic structure at the Fermi level.
Superlattices may play an important role in next generation electronic and spintronic devices if the key-challenge of the reading and writing data can be solved. This challenge emerges from the coupling of low dimensional individual layers with macro
scopic world. Here we report the study of the resistive switching characteristics of a of hybrid structure made out of a superlattice with ultrathin layers of two ferromagnetic metallic oxides, La0.7Sr0.3MnO3 (LSMO) and SrRuO3 (SRO). Bipolar resistive switching memory effects are measured on these LSMO/SRO superlattices, and the observed switching is explainable by ohmic and space charge-limited conduction laws. It is evident from the endurance characteristics that the on/off memory window of the cell is greater than 14, which indicates that this cell can reliably distinguish the stored information between high and low resistance states. The findings may pave a way to the construction of devices based on nonvolatile resistive memory effects.
سجل دخول لتتمكن من نشر تعليقات
التعليقات
جاري جلب التعليقات
سجل دخول لتتمكن من متابعة معايير البحث التي قمت باختيارها