Mn_5Ge_3C_x films with x>0.5 were experimentally shown to exhibit a strongly enhanced Curie temperature T_C compared to Mn_5Ge_3. In this letter we present the results of our first principles calculations within Greens function approach, focusing on the effect of carbon doping on the electronic and magnetic properties of the Mn_5Ge_3. The calculated exchange coupling constants revealed an enhancement of the ferromagnetic Mn-Mn interactions mediated by carbon. The essentially increased T_C in Mn_5Ge_3C is well reproduced in our Monte Carlo simulations and together with the decrease of the total magnetisation is found to be predominantly of an electronic nature.
قيم البحث
اقرأ أيضاً
We report Curie temperatures up to 150 K in annealed Ga1-xMnxAs epilayers grown with a relatively low As:Ga beam equivalent pressure ratio. A variety of measurements (magnetization, Hall effect, magnetic circular dichroism and Raman scattering) show
that the higher ferromagnetic transition temperature results from an enhanced free hole density. The data also indicate that, in addition to the carrier concentration, the sample thickness limits the maximum attainable Curie temperature in this material - suggesting that the free surface of Ga1-xMnxAs epilayers is important in determining their physical properties.
We report on an enhancement of the Curie temperature in GaMnAs/InGaMnAs superlattices grown by low-temperature molecular beam epitaxy, which is due to thin InGaMnAs or InGaAs films embedded into the GaMnAs layers. The pronounced increase of the Curie
temperature is strongly correlated to the In concentration in the embedded layers. Curie temperatures up to 110 K are observed in such structures compared to 60 K in GaMnAs single layers grown under the same conditions. A further increase in T$_C$ up to 130 K can be achieved using post-growth annealing at temperatures near the growth temperature. Pronounced thickness fringes in the high resolution X-ray diffraction spectra indicate good crystalline quality and sharp interfaces in the structures.
When comparing a set of La0.67Sr0.33MnO3 (LSMO) samples, the Curie temperature (TC) of the samples is an important figure of merit for the sample quality. Therefore, a reliable method to determine TC is required. Here, a method based on the analysis of the magnetization loops is proposed.
We provide experimental evidence that the upper limit of ~110 K commonly observed for the Curie temperature T_C of Ga(1-x)Mn(x)As is caused by the Fermi-level-induced hole saturation. Ion channeling, electrical and magnetization measurements on a ser
ies of Ga(1-x-y)Mn(x)Be(y)As layers show a dramatic increase of the concentration of Mn interstitials accompanied by a reduction of T_C with increasing Be concentration, while the free hole concentration remains relatively constant at ~5x10^20 cm^-3. These results indicate that the concentrations of free holes and ferromagnetically active Mn spins are governed by the position of the Fermi level, which controls the formation energy of compensating interstitial Mn donors.
We present a comparative, theoretical study of the doping dependence of the critical temperature $T_C$ of the ferromagnetic insulator-metal transition in Gd-doped and O-deficient EuO, respectively. The strong $T_C$ enhancement in Eu$_{1-x}$Gd$_x$O is
due to Kondo-like spin fluctuations on the Gd sites, which are absent in EuO$_{1-x}$. Moreover, we find that the $T_C$ saturation in Eu$_{1-x}$Gd$_x$O for large $x$ is due to a reduced activation of dopant electrons into the conduction band, in agreement with experiments, rather than antiferromagnetic long-range contributions of the RKKY interaction. The results shed light on possibilities for further increasing $T_C$.