We analyze the basic structural units of simple reconstructions of the (111) surface of SrTiO3 using density functional calculations. The prime focus is to answer three questions: what is the most appropriate functional to use; how accurate are the energies; what are the dominant low-energy structures and where do they lie on the surface phase diagram. Using test calculations of representative small molecules we compare conventional GGA with higher-order methods such as the TPSS meta-GGA and on-site hybrid methods PBE0 and TPSSh, the later being the most accurate. There are large effects due to reduction of the metal d oxygen sp hybridization when using the hybrid methods which are equivalent to a dynamical GGA+U, which leads to rather substantial improvements in the atomization energies of simple calibration molecules, even though the d-electron density for titanium compounds is rather small. By comparing the errors of the different methods we are able to generate an estimate of the theoretical error, which is about 0.25eV per 1x1 unit cell, with changes of 0.5-1.0 eV per 1x1 cell with the more accurate method relative to conventional GGA. An analysis of the plausible structures reveals an unusual low-energy TiO2-rich configuration with an unexpected distorted trigonal biprismatic structure. This structure can act as a template for layers of either TiO or Ti2O3, consistent with experimental results as well as, in principle, Magnelli phases. The results also suggest that both the fracture surface and the stoichiometric SrTiO3 (111) surface should spontaneously disproportionate into SrO and TiO2 rich domains, and show that there are still surprises to be found for polar oxide surfaces.
The release process for the fabrication of freestanding oxide microstructures relies on appropriate, controllable and repeatable wet etching procedures. SrTiO3 is among the most employed substrates for oxide thin films growth and can be decomposed in
In recent years, striking discoveries have revealed that two-dimensional electron liquids (2DEL) confined at the interface between oxide band-insulators can be engineered to display a high mobility transport. The recognition that only few interfaces
The so-called polar catastrophe, a sudden electronic reconstruction taking place to compensate for the interfacial ionic polar discontinuity, is currently considered as a likely factor to explain the surprising conductivity of the interface between t
The local structural distortions in polydomain ferroelectric PbTiO3/SrTiO3 superlattices are investigated by means of high spatial and energy resolution electron energy loss spectroscopy combined with high angle annular dark field imaging. Local stru
Strain can affect the morphology of a crystal surface, and cause modifications of its reconstruction even when weak, as in the case of mechanical bending. We carried out calculations of strain-dependent surface free energy and direct bending simulati