We report plane-polarized Raman scattering spectra of iron oxypnictide superconductor NdFeAsO$_{1-x}$F$_x$ single crystals with varying fluorine $x$ content. The spectra exhibit sharp and symmetrical phonon lines with a weak dependence on fluorine doping $x$. The temperature dependence does not show any phonon anomaly at the superconducting transition. The Fe related phonon intensity shows a strong resonant enhancement below 2 eV. We associate the resonant enhancement to the presence of an interband transition around 2 eV observed in optical conductivity. Our results point to a rather weak coupling between Raman-active phonons and electronic excitations in iron oxypnictides superconductors.
قيم البحث
اقرأ أيضاً
Hall effect and magnetoresistance have been measured on single crystals of $NdFeAsO_{1-x}F_{x}$ with x = 0 ($T_c$ = 0 $ $K) and x = 0.18 ($T_c$ = 50 $ $K). For the undoped samples, strong Hall effect and magnetoresistance with strong temperature depe
ndence were found below about 150 K. The magnetoresistance was found to be as large as 30% at 15 K at a magnetic field of 9 T. From the transport data we found that the transition near 155 K was accomplished in two steps: first one occurs at 155 K which may be associated with the structural transition, the second one takes place at about 140 K which may correspond to the spin-density wave like transition. In the superconducting sample with $T_c$ = 50 $ $K, it is found that the Hall coefficient also reveals a strong temperature dependence with a negative sign. But the magnetoresistance becomes very weak and does not satisfy the Kohlers scaling law. These dilemmatic results (strong Hall effect and very weak magnetoresistance) prevent to understand the normal state electric conduction by a simple multi-band model by taking account the electron and hole pockets. Detailed analysis further indicates that the strong temperature dependence of $R_H$ cannot be easily understood with the simple multi-band model either. A picture concerning a suppression to the density of states at the Fermi energy in lowering temperature is more reasonable. A comparison between the Hall coefficient of the undoped sample and the superconducting sample suggests that the doping may remove the nesting condition for the formation of the SDW order, since both samples have very similar temperature dependence above 175 K.
Raman spectra have been measured on iron-based quaternary CeO$_{1-x}$F$_x$FeAs and LaO$_{1-x}$F$_x$FeAs with varying fluorine doping at room temperatures. A group analysis has been made to clarify the optical modes. Based on the first principle calcu
lations, the observed phonon modes can be assigned accordingly. In LaO$_{1-x}$F$_x$FeAs, the E$_g$ and A$_{1g}$ modes related to the vibrations of La, are suppressed with increasing F doping. However F doping only has a small effect on the E$_g$ and A$_{1g}$ modes of Fe and As. The Raman modes of La and As are absent in rare-earth substituted CeO$_{1-x}$F$_x$FeAs, and the E$_g$ mode of oxygen, corresponding to the in-plane vibration of oxygen, moves to around 450 cm$^{-1}$ and shows a very sharp peak. Electronic scattering background is low and electron-phonon coupling is not evident for the observed phonon modes. Three features are found above 500 cm$^{-1}$, which may be associated with multi-phonon process. Nevertheless it is also possible that they are related to magnetic fluctuations or interband transitions of d orbitals considering their energies.
We use a magnetic force microscope (MFM) to investigate single vortex pinning and penetration depth in NdFeAsO$_{1-x}$F$_x$, one of the highest-$T_c$ iron-based superconductors. In fields up to 20 Gauss, we observe a disordered vortex arrangement, im
plying that the pinning forces are stronger than the vortex-vortex interactions. We measure the typical force to depin a single vortex, $F_{mathrm{depin}} simeq 4.5$ pN, corresponding to a critical current up to $J_c simeq 7 times 10^5$ A/cm$^2$. Furthermore, our MFM measurements allow the first local and absolute determination of the superconducting in-plane penetration depth in NdFeAsO$_{1-x}$F$_x$, $lambda_{ab}=320 pm 60$ nm, which is larger than previous bulk measurements.
This paper is no longer active and will NOT appear in print. For new data and analysis, please see: arXiv:0903.2220
The structural and magnetic phase transitions have been studied on NdFeAsO single crystals by neutron and x-ray diffraction complemented by resistivity and specific heat measurements. Two low-temperature phase transitions have been observed in additi
on to the tetragonal-to-orthorhombic transition at T_S = 142 K and the onset of antiferromagnetic (AFM) Fe order below T_N = 137 K. The Fe moments order AFM in the well-known stripe-like structure in the (ab) plane, but change from AFM to ferromagnetic (FM) arrangement along the c direction below T* = 15 K accompanied by the onset of Nd AFM order below T_Nd = 6 K with this same AFM configuration. The iron magnetic order-order transition in NdFeAsO accentuates the Nd-Fe interaction and the delicate balance of c-axis exchange couplings that results in AFM in LaFeAsO and FM in CeFeAsO and PrFeAsO.
سجل دخول لتتمكن من نشر تعليقات
التعليقات
جاري جلب التعليقات
سجل دخول لتتمكن من متابعة معايير البحث التي قمت باختيارها