We report studies on pressure dependence of superconducting transition temperature (Tc) of LaFeAsO, LaFeAs(O0.5F0.5) and LaFeAs(O0.89F0.11) samples. In-situ resistance measurements under high pressure showed that the Tc of these three compounds increases with pressure initially, reaches a maximum value and then decreases with further increasing pressure, although the Tc at ambient pressure are different. The onset Tc of LaFeAsO is ~50 K at 1.5 GPa, which is the highest record in La-based oxypnicited system. The significant change in Tc induced by pressure is attributed to the orbital degeneracy and the electron density of state at the Fermi level.
قيم البحث
اقرأ أيضاً
Electrical resistivity measurements under high pressures up to 29 GPa were performed for oxypnictide compound LaFeAsO. We found a pressure-induced superconductivity in LaFeAsO. The maximum value of Tc is 21 K at ~12 GPa. The pressure dependence of th
e Tc is similar to those of LaFeAsO1-xFx series reported previously.
The hydrostatic pressure effect on the newly discovered superconductor MgB2 has been determined. The transition temperature Tc was found to decrease linearly at a large rate of -1.6 K/GPa, in good quantitative agreement with the ensuing calculated va
lue of -1.4 K/GPa within the BCS framework by Loa and Syassen, using the full-potential linearlized augmented plane-wave method. The relative pressure coefficient, dlnTc/dp, for MgB2 also falls between the known values for conventional sp- and d-superconductors. The observation, therefore, suggests that electron-phonon interaction plays a significant role in the superconductivity of the compound.
Superconducting and structural phase transitions in a pyrochlore oxide Cd2Re2O7 are studied under high pressure by x-ray diffraction and electrical resistivity measurements. A rich P-T phase diagram is obtained, which contains at least two phases wit
h the ideal and slightly distorted pyrochlore structures. It is found that the transition between them is suppressed with increasing pressure and finally disappears at a critical pressure Pc = 3.5 GPa. Remarkable enhancements in the residual resistivity as well as the coefficient A of the AT 2 term in the resistivity are found around the critical pressure. Superconductivity is detected only for the phase with the structural distortion. It is suggested that the charge fluctuations of Re ions play a crucial role in determining the electronic properties of Cd2Re2O7.
Our recent study has revealed that the mixture of the dz2 orbital component into the Fermi surface suppresses Tc in the cuprates such as La2CuO4. We have also shown that applying hydrostatic pressure enhances Tc due to smaller mixing of the Cu4s comp
onent. We call these the orbital distillation effect. In our previous study, the 4s orbital was taken into account through the hoppings in the dx2-y2 sector, but here we consider a model in which of the dx2-y2, dz2 and 4s orbitals are all considered explicitly. The present study reinforces our conclusion that smaller 4s hybridization further enhances Tc.
High-quality polycrystalline samples of LaO0.5F0.5BiS2 were obtained using high-pressure synthesis technique. The LaO0.5F0.5BiS2 sample prepared by heating at 700 C under 2 GPa showed superconductivity with superconducting transition temperatures (Tc
) of Tconset = 11.1 and Tczero = 8.5 K in the electrical resistivity measurements and Tconset = 11.5 and Tcirr = 9.4 K in the magnetic susceptibility measurements, which are obviously higher than those of the LaO0.5F0.5BiS2 polycrystalline samples obtained using conventional solid-state reaction. It was found that the high-Tc phase can be stabilized under high pressure and relatively-low annealing temperature. X-ray diffraction analysis revealed that the high-Tc phase possessed a small ratio of lattice constants of a and c, c/a.