The iron oxyarsenide TbFeAsO0.85 was synthesized by a high-pressure method. A high-quality polycrystalline sample was obtained and characterized by measurements of magnetic susceptibility and electrical resistivity. Bulk superconductivity with Tc of 42 K was clearly established without an F doping usually conducted to tune on superconductivity in the iron oxypnictide.
قيم البحث
اقرأ أيضاً
A wide-range doping was achieved by a high-pressure method for TbFeAsO1-x from under doped to over doped superconducting compositions throughout the optimized superconductivity (Tc of 44 K). Tc vs. lattice constant shows a dome-shaped feature, while
Tc vs. the lattice constant likely follows a unique empirical curve over the doping range. The relatively large amount of oxygen vacancies up to 0.3 per the formula unit was introduced possibly because of the smaller replacement Tb than the other Ln (rare-earth element) in the LnFeAsO1-x system.
The transport and complex optical properties of the electron-doped iron-arsenic superconductor BaFe1.85Co0.15As2 with Tc = 25 K have been examined in the Fe-As planes above and below Tc. A Bloch-Gruneisen analysis of the resistivity yields a weak ele
ctron-phonon coupling constant lambda_ph ~ 0.2. The low-frequency optical response in the normal state appears to be dominated by the electron pocket and may be described by a weakly-interacting Fermi liquid with a Drude plasma frequency of omega_p,D ~ 7840 cm-1 (~ 0.972 eV) and scattering rate 1/tau_D ~ 125 cm-1 (~ 15 meV) just above Tc. The frequency-dependent scattering rate 1/tau(omega) has kinks at ~ 12 and 55 meV that appear to be related to bosonic excitations. Below Tc the majority of the superconducting plasma frequency originates from the electron pocket and is estimated to be omega_p,S ~ 5200 cm-1 (lambda0 ~ 3000 Angstroms) for T << Tc, indicating that less than half the free carriers in the normal state have collapsed into the condensate, suggesting that this material is not in the clean limit. Supporting this finding is the observation that this material falls close to the universal scaling line for a BCS dirty-limit superconductor in the weak-coupling limit. There are two energy scales for the superconductivity in the optical conductivity and photo-induced reflectivity at Delta1 ~ 3.1 +/- 0.2 meV and Delta2 ~ 7.4 +/- 0.3 meV. This corresponds to either the gaping of the electron and hole pockets, respectively, or an anisotropic s-wave gap on the electron pocket; both views are consistent with the s+/- model.
Electrical-resistivity and magnetic-susceptibility measurements under hydrostatic pressure up to p = 2.75 GPa have been performed on superconducting LiFeP. A broad superconducting (SC) region exists in the temperature - pressure (T-p) phase diagram.
No indications for a spin-density-wave transition have been found, but an enhanced resistivity coefficient at low pressures hints at the presence of magnetic fluctuations. Our results show that the superconducting state in LiFeP is more robust than in the isostructural and isoelectronic LiFeAs. We suggest that this finding is related to the nearly regular [FeP_4] tetrahedron in LiFeP.
77Se and 87Rb nuclear magnetic resonance (NMR) experiments on Rb0.74Fe1.6Se2 reveal clearly distinct spectra originating from a majority antiferromagnetic (AF) and a minority metallic-superconducting (SC) phase. The very narrow NMR line of the SC pha
se evidences the absence of Fe vacancies and any trace of AF order. The Rb content of the SC phase is deduced from intensity measurements identifying Rb0.3(1)Fe2Se2 as the actual composition of the SC fraction. The resulting estimate of 0:15 electrons/Fe brings this class of superconductors 245 family closer to the other Fe-based superconductor families.
One of the most important properties of very recently reported FeSe based superconductors is the robustness of their superconductivity under applied magnetic field. The synthesis and control of superconductivity in FeSe based compounds is rather a di
fficult task. Synthesis and physical property characterization for optimized superconductivity of FeSe1/2Te1/2 at 13 K is reported here. The compound crystallized in a tetragonal structure with lattice parameters a = 3.8008(10) and c = 6.0187 (15) A. Magnetization measurements indicated bulk superconductivity with lower critical field (Hc1) of around 180 Oe. By applying Ginzburg Landau (GL) theory, the Hc2(0) value is estimated to be = 1840 kOe for the 90% of resistive transition. A heat capacity measurement revealed bulk superconductivity by a hump at Tc near 13 K, and an expected decrease was observed under an applied magnetic field.
سجل دخول لتتمكن من نشر تعليقات
التعليقات
جاري جلب التعليقات
سجل دخول لتتمكن من متابعة معايير البحث التي قمت باختيارها