Two new phases YbCu4.4 and YbCu4.25 are found as a result of careful phase diagram investigations. Between the congruent and peritectic formation of YbCu4.5 and YbCu3.5, respectively, the phases YbCu4.4 and YbCu4.25 are formed peritectically at 934(2)degC and 931(3)degC. Crystal growth was realised using a Bridgman technique and single crystalline grains of about 50-100 10^{-6}m were analyzed by electron diffraction and single crystal X-ray diffraction. Due to the only slight differences in both compositions and formation temperatures the growth of larger single crystals of a defined superstructure is challenging. The compounds YbCu4.4 and YbCu4.25 fit in Cerny`s (J. Solid State Chem. 174 (2003) 125) building principle {(RECu5)n(RECu2)} where RE = Yb with n = 4 and 3. YbCu4.4 and YbCu4.25 base on AuBe5/MgCu2-type substructures and contain approximately 4570 and 2780 atoms per unit cell. The new phases close the gap in the series of known copper-rich rare earth compounds for n = 1, 2 (DyCu3.5, DyCu4.0) and n = 5 (YbCu4.5, DyCu4.5).
قيم البحث
اقرأ أيضاً
We present a tutorial on the principles of crystal growth of intermetallic and oxide compounds from molten solutions, with an emphasis on the fundamental principles governing the underlying phase equilibria and phase diagrams of multicomponent systems.
The use of oxide materials in oxide electronics requires their controlled epitaxial growth. Recently, it was shown that Reflection High Energy Electron Diffraction (RHEED) allows to monitor the growth of oxide thin films even at high oxygen pressure.
Here, we report the sub-unit cell molecular or block layer growth of the oxide materials Sr2RuO4, MgO, and magnetite using Pulsed Laser Deposition (PLD) from stoichiometric targets. Whereas for perovskites such as SrTiO3 or doped LaMnO3 a single RHEED intensity oscillation is found to correspond to the growth of a single unit cell, in materials where the unit cell is composed of several molecular layers or blocks with identical stoichiometry, a sub-unit cell molecular or block layer growth is established resulting in several RHEED intensity oscillations during the growth of a single unit-cell.
alpha-Fe single crystals of rhombic dodecahedral habit were grown from a melt of Li$_{84}$N$_{12}$Fe$_{sim 3}$. Crystals of several millimeter along a side form at temperatures around $T approx 800^circ$C. Upon further cooling the growth competes wit
h the formation of Fe-doped Li$_3$N. The b.c.c. structure and good sample quality of alpha-Fe single crystals were confirmed by X-ray and electron diffraction as well as magnetization measurements and chemical analysis. A nitrogen concentration of 90,ppm was detected by means of carrier gas hot extraction. Scanning electron microscopy did not reveal any sign of iron nitride precipitates.
Crystal and magnetic structures of a series of novel quantum spin trimer system Ca3Cu3xNix(PO4)4 (x=0,1,2) were studied by neutron powder diffraction at the temperatures 1.5-290 K. The composition with one Ni per trimer (x=1) has a monoclinic structu
re (space group P 21 /a, no. 14) with the unit cell parameters a = 17.71 A, b = 4.89 A, c = 8.85 A and = 123.84 deg at T=290 K. The (x=2) composition crystallizes in the C 2/c space group (no. 15) with the doubled unit cell along c-axis. Each trimer is formed by two crystallographic positions: one in the middle and the second one at the ends of the trimer. We have found that the middle position is occupied by the Cu2+, whereas the end positions are equally populated with the Cu2+ and Ni2+ for (x=1) while in the (x=2) the trimers were found to be of only one type Ni-Cu-Ni. Below TN = 20 K the (x=2) compound shows an antiferromagnetic ordering with propagation vector star {[1/2,1/2, 0], [-1/2,1/2, 0]} The magnetic structure is very well described with the irreducible representation tau22 using both arms of the star {k} with the magnetic moments 1.89(1) muB and 0.62(2) muB for Ni2+ and Cu2+ ions, respectively. We note that our powder diffraction data cannot be fitted by a model containing only one arm of the propagation vector star. The Cu/Ni-spins form both parallel and antiparallel configurations in the different trimers, implying substantial effect of the inter-trimer interaction on the overall magnetic structure.
The resistive and reactive components of magneto-impedance (MI) for Finemet/Copper/Finemet sandwiched structures based on stress-annealed nanocrystalline Fe75Si15B6Cu1Nb3 ribbons as functions of different fields (longitudinal and perpendicular) and f
requencies have been measured and analyzed. Maximum magneto-resistance and magneto-inductance ratios of 700% and 450% have been obtained in 30-600 kHz frequency range respectively. These large magneto-resistance and magneto-inductive ratios are a direct consequence of the large effective relative permeability due to the closed magnetic flux path in the trilayer structure. The influence of perpendicular bias fields (Hper) in the Longitudinal Magneto-impedance (LMI) configuration greatly improves the MI ratios and sensitivities. The maximum MI ratio for the resistive part increases to as large as 2500% for Hper ~ 1 Oe. The sensitivity of the magneto-resistance increases from 48%/Oe to 288%/Oe at 600 kHz frequency with the application of Hper ~ 30 Oe. Such high increase in MI ratios and sensitivities with perpendicular bias fields are due to the formation the favourable (transverse) domain structures.
سجل دخول لتتمكن من نشر تعليقات
التعليقات
جاري جلب التعليقات
سجل دخول لتتمكن من متابعة معايير البحث التي قمت باختيارها