The newly discovered iron-based superconductors have stimulated enormous interests in the field of superconductivity. Since the new superconductor is a layered system, the anisotropy is a parameter with the first priority to know. Meanwhile any relevant message about the critical fields (upper critical field and irreversibility line) are essentially important. By using flux method, we have successfully grown the single crystals NdO0.82F0.18FeAs at ambient pressure. Resistive measurements reveal a surprising discovery that the anisotropy Gamma = (mc/mab)^{1/2} is below 5, which is much smaller than the theoretically calculated results. The data measured up to 400 K show a continuing curved feature which prevents a conjectured linear behavior for an unconventional metal. The upper critical fields determined based on the Werthamer-Helfand-Hohenberg formula are H_{c2}^{H||ab}(T=0 K) = 304 T and H_{c2}^{H||c}(T=0 K)=62-70 T, indicating a very encouraging application of the new superconductors.
قيم البحث
اقرأ أيضاً
Superconductivity of Ca1-xLaxFe2As2 single crystals with various doping level were investigated via electromagnetic measurements for out-plane (H//c) and in-plane (H//ab) directions. Obvious double superconducting transitions, which can survive in ma
gnetic fields up to several Tesla, were observed in the medium-doped (x = 0.13) sample. Two kinds of distinct Hc2 phase diagrams were established for the low superconducting phase with Tc lower than 15 K and the high superconducting phase with Tc of over 40 K, respectively. Both the two kinds of phase diagrams exist in the medium-doped sample. Unusual upward curvature near Tc was observed in Hc2 phase diagrams and analyzed in detail. Temperature dependences of anisotropy for different doping concentrations were obtained and compared. Both superconducting phases manifest extremely large anisotropies, which may originate from the interface or intercalation superconductivity.
We present heat capacity measurements of the upper critical fields of single-crystal NdFeAsO1-xFx. In zero-magnetic field a clear step in the heat capacity is observed at Tc = 47K . In fields applied perpendicular to the FeAs-layers the step broadens
significantly whereas for the in-plane orientation the field effects are small. This behavior is reminiscent of the CuO2-high-Tc superconductors and is a manifestation of pronounced fluctuation effects. Using an entropy conserving construction we determine the transition temperatures in applied fields and the upper critical field slopes of dHc2,a = -0.72 T/K and dHc2,ab = -3.1 T/K. Zero-temperature coherence lengths of xiab = 3.7 nm and xic = 0.9 nm and a modest superconducting anisotropy of gamma ~ 4 can be deduced in a single-band model.
Optimally-doped La1.85Sr0.15CuO4 single crystals have been investigated by dc and ac magnetic measurements. These crystals have rectangular needle-like shapes with the long needle axis parallel to the crystallographic c axis (c-crystal) or parallel t
o the basal planes (a-crystal). In both crystals, the temperature dependence of the upper critical fields (HC2) and the surface critical field (HC3) were measured. The H-T phase diagram is presented. Close to TC =35 K, for the c-crystal, {gamma}c = / = 1.80(2), whereas for the a-crystal the {gamma}a = / =4.0(2) obtained, is much higher than the theoretical value 1.69. At low applied dc fields, positive field-cooled branches known as the paramagnetic Meissner effect (PME) are observed, their magnitude is inversely proportional to H. The anisotropic PME is observed in both a- and c-crystals, only when the applied field is along the basal planes. It is speculated that the high {gamma}a and the PME are connected to each other.
Despite the intense activity in the year since the discovery of superconductivity in MgB2, key parameters, in particular the upper and lower critical fields Hc2 and Hc1 and their anisotropies, are not well-established, largely because of the difficul
ty of growing MgB2 crystals. Attempts have been made to deduce these parameters from experiments on polycrystalline material, but they have substantial uncertainties. Hc2 is particularly important for applications, as it is the field which quenches bulk super-conductivity. In terms of understanding MgB2, it is now clear that the conventional electron-phonon interaction is strong enough to account for the high transition temperature Tc, but the consequences of the double super-conducting gap for the anisotropy and its dependence on temperature, are uncertain. Here we describe detailed direct measurements of Hc1(T) and Hc2(T) for the two principal crystallographic directions in a clean single crystal of MgB2. For fields in the c-direction, $mu_0 H^c_{c1}(0)$ = $0.28 +- 0.01T$ and $mu_0 H^c_{c2}(0)$ is $3 +- 0.5T$; this ratio of critical fields is rather low and implies that MgB2 is only just a Type II super-conductor. The anisotropies of both critical fields are close to 2.
Sizable single crystals of $BaFe_2As_2$ have been grown with self-flux method. The crystals are plate-like with c-axis perpendicular to the plane. The size can be as large as 3 x 5 x 0.2 $mm^3$. The resistivity anisotropy ($rho_c/rho_{ab}$) is as lar
ge as about 150, and independent of temperature. The transport in ab plane and along c-axis direction shares the same scattering mechanism. In contrast to the magnetic behavior of polycrystalline samples, no Curie-Weiss behavior are observed, a temperature linear dependent susceptibility occurs above spin-density-wave (SDW) transition. The susceptibility behavior is very similar to that of antiferromagnetic SDW chromium. Magnetic behavior of single crystal definitely gives evidence for existence of local moment except for the contribution to susceptibility from itinerant electrons. A resistivity minimum strongly dependent on magnetic field is observed. A log(1/T) divergency, similar to that of the underdoped cuprates, happens at low temperature. Here we first present intrinsic transport and magnetic properties, and their anisotropy from high quality single crystal.