In this report we show that in the perovskite manganite La_{1-x}Ca_{x}MnO_3 for a fixed x approx 0.33, the magnetic transition changes over from first order to second order on reducing the particle size to nearly few tens of a nanometer. The change-over is brought about only by reducing the size and with no change in the stoichiometry. The size reduction to an average size of about 15 nm retains the ferromagnetic state albeit with somewhat smaller saturation magnetization and the ferromagnetic transition temperature T_{C} is suppressed by a small amount (4%). The magnetization of the nanoparticles near T_{C} follow the scaling equation $M/|epsilon|^beta = f_pm(H/|epsilon|^{gamma+beta})$, where, $epsilon = |T-T_C|/T_C$. The critical exponents, associated with the transition have been obtained from modified Arrott plots and they are found to be $beta=0.47pm 0.01$ and $gamma=1.06pm 0.03$. From a plot of M vs H at T_{C} we find the exponent $delta=3.10 pm 0.13$. All the exponents are close to the mean field values. The change-over of the order of the transition has been attributed to a lowering of the value of the derivative dT_{C}/dP due to an increased pressure in the nanoparticles arising due to size reduction. This effect acts in tandem with the rounding off effect due to random strain in the nanoparticles.
قيم البحث
اقرأ أيضاً
Taking the pseudobinary C15-Laves phase compound Ce(Fe$_{0.96}$Al$_{0.04}$)$_2$ as a paradigm for studying a ferromagnetic(FM) to antiferromagnetic(AFM) phase transition, we present interesting thermomagnetic history effects in magnetotransport measu
rements across this FM-AFM transition. We argue that these distinctive hysteretic features can be used to identify the exact nature -first order or second order - of this kind of transition in magnetic systems where electrical transport is strongly correlated with the underlying magnetic order. A comparison is made with the similar FM-AFM transitions observed in Nd and Pr-based manganese compounds with perovskite-type structure.
Taking the pseudobinary C15 Laves phase compound Ce(Fe$_{0.96}$Al$_{0.04}$)$_2$ as a paradigm for studying a ferromagnetic to antiferromagnetic phase transition, we present interesting thermomagnetic history effects in magnetotransport as well as mag
netisation measurements across this phase transition. A comparison is made with history effects observed across the ferromagnetic to antiferromagnetic transition in R$_{0.5}$Sr$_{0.5}$MnO$_3$ crystals.
Cubic spinel GeNi2O4 exhibits intriguing magnetic properties with two successive antiferromagnetic phase transitions (TN1 12.1 and TN2 11.4 K) with the absence of any structural transition. We have performed detailed heat capacity and magnetic measur
ements in different crystallographic orientations. A new magnetic phase in presence of magnetic field (H > 4 T) along the [111] direction is revealed, which is not observed when the magnetic field is applied along the [100] and [110] directions. High field neutron powder diffraction measurements confirm such a change in magnetic phase, which could be ascribed to a spin reorientation in the presence of magnetic field. A strong magnetic anisotropy and competing magnetic interactions play a crucial role on the complex magnetic behavior in this cubic system.
Epitaxial strain and chemical substitution have been the workhorses of functional materials design. These static techniques have shown immense success in controlling properties in complex oxides through the tuning of subtle structural distortions. Re
cently, an approach based on the excitation of an infrared active phonon with intense mid-infrared light has created an opportunity for dynamical control of structure through special nonlinear coupling to Raman phonons. We use first-principles techniques to show that this approach can dynamically induce a magnetic phase transition from the ferromagnetic ground state to a hidden antiferromagnetic phase in the rare earth titanate GdTiO$_3$ for realistic experimental parameters. We show that a combination of a Jahn-Teller distortion, Gd displacement, and infrared phonon motion dominate this phase transition with little effect from the octahedral rotations, contrary to conventional wisdom.
X-ray diffraction, resistivity, ac susceptibility and magnetization studies on La0.67Ca0.33Mn1-xRuxO3 (0 x < 0.1) were carried out. A significant increase in the lattice parameters indicated the presence of mixed valance state of Ru: Ru3+ and Ru4+. T
he resistivity of the doped compounds exhibited two features: a broad maximum and a relatively sharp peak. While a para to ferromagnetic transition could be observed for the latter peak, no magnetic signal either in ac susceptibility or in magnetization measurements could be observed for the broad maximum. The magnetic moment decreases non linearly from 3.55 to 3 mB over the Ru composition from 0 to 8.5 at.%. Based on the results of the present studies and on existing literature on the Mn-site substituted systems, we argue that a magnetic phase separation occurs in the Ru doped system. While the sharp peak in the resistivity corresponds to Ru4+ enriched region with a ferromagnetic coupling with neighboring Mn ions, the broad peak corresponds to a Ru3+ rich regions, with an antiferromagnetic coupling with neighboring Mn ions.