The CoO$_{2}$ layers in sodium-cobaltates Na$_{x}$CoO$_{2}$ may be viewed as a spin $S=1/2$ triangular-lattice doped with charge carriers. The underlying physics of the cobaltates is very similar to that of the high $T_{c}$ cuprates. We will present unequivocal $^{59}$Co NMR evidence that below $T_{CO}sim51 K$, the insulating ground state of the itinerant antiferromagnet Na$_{0.5}$CoO$_{2}$ ($T_{N}sim 86 K$) is induced by charge ordering.
قيم البحث
اقرأ أيضاً
The magnetic and transport properties are systematically studied on the single crystal $Na_{0.55}CoO_2$ with charge ordering and divergency in resistivity below 50 K. A long-range ferromagnetic ordering is observed in susceptibility below 20 K with t
he magnetic field parallel to Co-O plane, while a negligible behavior is observed with the field perpendicular to the Co-O plane. It definitely gives a direct evidence for the existence of in-plane ferromagnetism below 20 K. The observed magnetoresistance (MR) of 30 % at the field of 6 T at low temperatures indicates an unexpectedly strong spin-charge coupling in triangle lattice systems.
Charge ordering behavior is observed in the crystal prepared through the immersion of the $Na_{0.41}CoO_2$ crystal in distilled water. Discovery of the charge ordering in the crystal with Na content less than 0.5 indicates that the immersion in water
brings about the reduction of the $Na_{0.41}CoO_2$. The formal valence of Co changes from +3.59 estimated from the Na content to +3.5, the same as that in $Na_{0.5}CoO_2$. The charge compensation is confirmed to arise from the intercalation of the oxonium ions as occurred in the superconducting sodium cobalt oxide bilayer-hydrate.cite{takada1} The charge ordering is the same as that observed in $Na_{0.5}CoO_2$. It suggests that the Co valence of +3.5 is necessary for the charge ordering.
Susceptibility, specific heat, and muon spin rotation measurements on high-quality single crystals of $rm Na_{0.82}CoO_2$ have revealed bulk antiferromagnetism with N{e}el temperature $rm T_N = 19.8 pm 0.1$ K and an ordered moment perpendicular to th
e $rm CoO_2$ layers. The magnetic order encompasses nearly 100% of the crystal volume. The susceptibility exhibits a broad peak around 30 K, characteristic of two-dimensional antiferromagnetic fluctuations. The in-plane resistivity is metallic at high temperatures and exhibits a minimum at $rm T_N$.
We present the results of measurements of the dc-magnetic susceptibility chi(T) and the 23Na-NMR response of Na_{0.70}CoO_{2} at temperatures between 50 and 340 K. The chi(T) data suggest that for T > 75 K, the Co ions adopt an effective configuratio
n of Co^{3.4+}. The 23Na-NMR response reveals pronounced anomalies near 250 and 295 K, but no evidence for magnetic phase transitions is found in chi(T). Our data suggest the onset of a dramatic change in the Co 3d-electron spin dynamics at 295 K. This process is completed at 230 K. Our results maybe interpreted as evidence for either a tendency to electron localization or an unconventional charge-density wave phenomenon within the cobalt oxide layer, CoO_2, 3d electron system near room temperature.
We performed $^{59}$Co nuclear magnetic and quadrupole resonance (NMR and NQR) measurements under pressure on a single-crystalline CeCoSi, which undergoes an unresolved phase transition at $T_0$. The NQR spectra clearly showed that the phase transiti
on at $T_0$ is nonmagnetic, but any symmetry lowering at the Co site was not seen irrespective of the feature of second-order phase transition. By contrast, the NMR spectra were split by the induced magnetic field perpendicular to the external magnetic field. These results show that the phase below $T_0$ is not a simple paramagnetic state but is most likely electric multipolar ordered state of Ce $4f$ electrons. The development of the Kondo effect by applying pressure is thought to be crucial to stabilize this state and to show novel features beyond commonality of tetragonal Ce-based systems.